Loctite 3D IND147 HDT230 Black - Certified For Carbon Printers

Mechanical Properties

Measure

Method

Green

Post Processed

Tensile Stress at Break

MPa

ASTM D638

31 ± 2[2] 

67 ± 16 [1]

Young’s Modulus

MPa

ASTM D638

1150 ± 160 [2]

3190 ± 80 [1]

Elongation at Break

%

ASTM D790

6 ± 2[2]

2.4 ± 0.7 [1]

Flexural Modulus

MPa

ASTM D790

1170 ± 100 [11]

3690 ± 60 [12]

Flexural Stress at Break MPa ASTM D790 60 ± 4

MPa

ASTM D790

60 ± 4[11]

120 ± 4[12]

Flexural Strain at Break 

%

ASTM D790

9.7 ± 0.5 [11] 

3.5 ± 0.2 [12]

IZOD Impact Strength(Notched)

J/m

ASTM D256 

-

14.6 ± 0.1[7]

Shore Hardness (3s) 

D

ASTM D2240

-

94 [8]

Thermal Properties

Measure

Method

Green

Post Processed

HDT at 0.455 MPa 

° C

ASTM D648

-

291 ± 15 [13]

HDT at 1.82 MPa 

° C

ASTM D648

-

163 ± 4 [14]

Thermal Conductivity

W/9(m•K)

ASTM D5930

-

0.20 [5]

Heat Capacity

J/(g•K)

ASTM D5930

-

1.3 [5]

Coefficient of Thermal Expansion (25 - 200° C)

μm/m-°C

ASTM E831

-

114. [6]

Other Properties

Measure

Method

Green

Post Process

Water Absorption (24hr)

%

ASTM D570

-

0.25 [9]

Solid Density

g/cm³

ASTM D1475

1.25 [10]

1.26 [10]

Electrical Properties

Measure

Method

Green

Post Processed

Dielectric Strength

kV/mm

ASTM D149

-

29 ± 2 [1]

Dielectric Constant (50 Hz)

-

ASTM D150

-

3.0 [2]

Dielectric Constant (1 kHz)

-

ASTM D150

-

3.0 [2]

Dielectric Constant (1 MHz)

-

ASTM D150

-

2.8 [2]

Dissipation Factor (50 Hz)

-

ASTM D150

-

-0.002 [2]

Dissipation Factor (1 kHz)

-

ASTM D150

-

0.008 [2]

Dissipation Factor (1 MHz)

-

ASTM D150

-

0.016 [2]

Volume Resistivity

Ω•cm

ASTM D257

-

3.56 E + 16 [3]

Surface Resistivity

Ω

ASTM D257

-

3.38 E + 16 [3]

Liquid Properties

Measure

Method

Value

Viscosity at 25° C (77°F)

cP

ASTM D7867

2105 ± 200 [4]

Liquid Density

g/cm3

ASTM D1475

1.15 [5]