LOCTITE 3D | IND147 HDT230 High Heat
The Henkel LOCTITE 3D IND147 HDT230 High Heat is a durable resin, created for the use in tooling and molding applications. This material is very heat resistant. The LOCTITE 3D IND147 HDT230 is available in black.
£260.00
Tax included
Free lifetime remote support on all products
Ask us about our discounts for education
The LOCTITE 3D IND147 HDT230 High Heat
The IND147 HDT230 is a tough resin with high temperature resistance, perfect for tooling and molding applications. The material is stable with a great surface finish and can withstand mechanical stresses.
Key Features
- High Heat Deflection Temperature
- Tough with goos dimensional stability
- Good surface finish
| Mechanical Properties | Method | Green | Dymax 5000 (10 min. per side) | Dymax 5000 (10 min. per side) 170°C for 3 hours |
|---|---|---|---|---|
| Tensile Stress at Break | ASTM D638 | 30.7 ± 1.6 MPa | 75 ± 2.0 MPa | 84 ± 4.7 MPa |
| Young's Modulus | ASTM D638 | 1150 ± 137 MPa | 3192 ± 35MPa | 3285 ± 131MPa |
| Elongation at Failure | ASTM D638 | 5.9 ± 1.7 % | 3.0 ± 0.1 % | 3.2 ± 0.3 % |
| Flexural Stress at Yield | ASTM D790 | 68 ± 3 MPa | 130 ± 11 MPa | 126 ± 11 MPa |
| Flexural Modulus | ASTM D790 | 2053 ± 189 | 3835 ± 131 MPa | 3926 ± 51 MPa |
| Flexural Strain at Break | ASTM D790 | 7.6 ± 2.7 % | 3.1 ± 0.4 % | 3.2 ± 0.3 % |
| Thermal Properties | Method | Green | Dymax 5000 (10 min. per side) | Dymax 5000 (10 min. per side) 170°C for 3 hours |
|---|---|---|---|---|
| HDT at 0.455 MPa DMA | Internal | 56.1° C | 140° C | 237° C |
| HDT at 1.82 MPa DMA | Internal | 111° C | 166.7° C | |
| HDT at 0.455 MPa VICAT | ASTM D648 | 230.6° C | ||
| HDT at 1.82 MPa VICAT | ASTM D648 | |||
| Coefficient of Thermal Expansion (25 - 200° C) | ASTM E831 | 114μm/m-°C | 106μm/m-°C |
| Other Properties | Method | Green | Dymax 5000 (10 min. per side) | Dymax 5000 (10 min. per side) 170°C for 3 hours |
|---|---|---|---|---|
| Durometer (Shore D, 0 sec) | ASTM D2240 | 94D | 94.5D | |
| IZOD Impact Strength | ASTM D256 | 14.6 J/m | 14.5 J/m | |
| Water Absorption (24 hr) | ASTM D570 | 0.25 % | ||
| Solid Density | ASTM D792 | 1.246 g/cm³ | 1.262 g/cm³ | |
| Shrinkage by Density | ASTM D792 | 8.25 % | 9.64 % |
| Liquid Properties | Method | Green | Dymax 5000 (10 min. per side) | Dymax 5000 (10 min. per side) 170°C for 3 hours |
|---|---|---|---|---|
| Viscosity at 25° C | ASTM D7867 | 2105 ± 200 cP | ||
| Liquid Density | ASTM D1475 | 1.15 g/mL |
Data sheet
- Young’s Modulus (MPa)
- 30.7 ± 1.6 MPa
You might also like
The Henkel LOCTITE 3D IND147 HDT230 High Heat is a durable resin, created for the use in tooling and molding applications. This material is very heat resistant. The LOCTITE 3D IND147 HDT230 is available in black.