Henkel LOCTITE 3D IND403 HDT80 High Modulus is a tough resin for applications in tooling production. The material has great surface finish and can withstand mechanical stresses. It is available in black.
276,00 €
Bruttopreis
Kostenloser lebenslanger Remote-Support für alle Produkte
Fragen Sie uns nach unseren Bildungsrabatten
The LOCTITE 3D IND403 HDT80 High Modulus Resin
The IND403 is a temperature resistant resin that showcases an excellent surface finish and outstanding dimensional accuracy. Due to these features the LOCTITE 3d IND403 HDT80 is recommended for use in tooling production for low temperature processes. This resin is stress resistant and can withstand high chemical stressors while maintaining dimensional stability, which additionally makes it the ideal material for interior applications.
Key Features
- High heat deflection temperature, HDT 80° C
- Tough material
- Good dimensional stability
- Good surface finish
| Mechanical Properties | Method | Green | Post Processed |
|---|---|---|---|
| Tensile Stress at Yield | ASTM D638 | 56.1 ± 8 MPa | 91 ± 2 MPa |
| Tensile Stress at Break | ASTM D638 | 46.5 ± 2.5 MPa | 87 ± 3 MPa |
| Young's Modulus | ASTM D638 | 2176 ± 72 MPa | 2750 ± 65 MPa |
| Elongation at Failure | ASTM D638 | 15 ± 10 % | 8.5 ± 2 % |
| Maximum Flexural Stress | ASTM D790 | 81 ± 2 | 136 ± 1.5 MPa |
| Flexural Modulus | ASTM D790 | 1879 ± 34 | 2880 ± 50 MPa |
| Flexural Strain at Break | ASTM D790 | > 10 % | > 10 % |
| Impact Strength - IZOD Notched | ASTM D256 | 27.2 ± 4.7 | |
| Impact Strength - IZOD Unnotched | ASTM D256 | > 250 |
| Other Properties | Method | Green | Post Processed |
|---|---|---|---|
| Hardness Shore D (0, 3 seconds) | ASTM D2240 | 81D, 76D | 80D, 78D |
| Solid Density | ASTM D1475 | 1.17 g/cm³ | 1.20 g/cm³ |
| Volumetric Shrinkage | Internal | 8.67 % | 10.99 % |
| Thermal Conductivity | ASTM D5930 | 0.22 W/m*K | |
| Heat Capacity | ASTM D5930 | 1.35 J/g*K | |
| Heat Deflection Temperature at 0.455 MPa | ASTM D648 | 64 ± 1.6° C | 81.7 ± 1° C |
| Heat Deflection Temperature at 1.82 MPa | ASTM D648 | 64.7° C | |
| Viscosity at 25° C | ASTM D7867 | 100 ± 200 cP | |
| Liquid Density | ASTM D1475 | 1.08 g/mL |
Technische Daten
- Young’s Modulus (MPa)
- 2176 ± 72 MPa / 2750 ± 65 MPa
- Liquid Density
- 1.08 g/mL